1.基层必须平整坚固，不得有油脂、起砂、空鼓、脱落等现象，基层不平整处和麻面应用腻子刮平方可进行涂料施工。

 2.墙面很平整可不批刮腻子，直接用砂纸打磨表面除去表面尘粒。

 3.墙面比较粗糙可先用铲刀把突出的部位铲平，然后刮两遍腻子。

 工艺流程：基层处理→刮腻子找平→封闭底漆→第一遍面漆→第二遍面漆

 1.腻子批涂完要足够干燥才能进行刷漆工序间＞24小时，气温较低时要适当延长，如果是旧墙翻新，在涂饰涂料前应清除疏松的旧装饰层。刷漆每道工序之间至少间隔2-4小   时，如果气温较低应延长间隔时间。

 2.施工前漆料必须搅拌均匀。

稀释

 使用前应搅拌均匀。为达到最佳涂刷效果，刷涂、辊涂时通常可加入涂料0%-10%体积的水，并搅拌均匀。（可根据施工手感酌情增减）

清洗

 涂装中途停顿及涂装完毕后，请及时使用清水清洗所有器具。

注意事项

 请不要在潮湿或寒冷的天气（气温低于5°C，相对湿度大于85%）情况下施工，否则不能达到预期的涂装效果。

Coating parameters:

 1.The base layer must be flat and firm, free of grease, sand, hollowing, peeling and other   phenomena. The uneven and pockmarked surface of the base layer can be coated with putty.

 2.If the wall is very flat, it is not necessary to apply putty, and directly use sandpaper to   polish the surface to remove dust particles.

 3. If the wall surface is rough, use a shovel to level the protruding part first, and then apply   putty twice.

 Process flow: base treatment → puttying and leveling → sealing primer → first finishing coat → second finishing coat

 1.After the putty is applied in batches, it should be dry enough to carry out the painting process. The interval between the painting processes should be more than 24 hours. When the temperature is low, it should be extended appropriately. If the old wall is renovated, the loose old decorative layer should be removed before painting. The interval between each painting process shall be at least 2-4 hours, and the interval shall be extended if the temperature is low.

 2.The paint must be mixed evenly before construction.

Dilution:

 Mix evenly before use. In order to achieve the best brushing effect, 0% - 10% volume of water can be added to the coating during brushing and roller coating, and mixed evenly. (It can be increased or decreased according to the construction feel)

Wash：

 Please use clean water to clean all appliances in a timely manner when painting is stopped and finished.

Matters needing attention：

 Please do not work in wet or cold weather (temperature lower than 5 ° C, relative humidity greater than 85%), otherwise the expected coating effect cannot be achieved.